Orthopaedic screws

ABSTRACT

An orthopaedic screw having a plurality of regions, at least one of which may be porous. The orthopaedic screw includes a head, a tip and at least one thread. The porosity of the screw of the present invention can vary within the part or region, including changes in pore shape, size and density. These characteristics can vary along the length of the screw axis and/or radially (from the outer diameter to the axis). The orthopaedic screw may further include at least one solid region formed of any implantable polymer, reinforced polymer or metal.

CROSS REFERENCE TO RELATED APPLICATIONS

This is a non-provisional application based upon U.S. provisional patent application Ser. No. 61/088,383, entitled “ORTHOPAEDIC SCREWS”, filed Aug. 13, 2008, which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to orthopaedic devices, and, more particularly, to orthopedic screws.

2. Description of the Related Art

A number of solid metal and resorbable polymer (e.g. PLLA, PGA) screws are known. These screws are generally meant to provide short term (9 months or less) attachment of the soft tissue to the bone until healing and integration can occur.

There are a number of problems associated with the known metal and resorbable screws. Due to the density of the metals that are used in the solid metal screws, it is difficult to examine bone or soft tissue that is near the screw via x-ray, CT, or MRI scan. The screw causes a significant ‘white-out’ in the region of the screw. Tissue healing and integration around the screw is critical to the success of the surgery, thus the ability to evaluate the tissue near the screw is valuable. In addition, the solid metal screws have issues with poor initial fixation and later pull-out of the soft tissue (e.g. pull out of an ACL from the bone) does occur. These are painful and can require follow-up surgery. Certainly any improvements to reduce the rate of pull-out and additional surgery would be desirable.

With respect to the known resorbable screws, issues with poor initial fixation and pull-out also exist. The rate of resorbtion of the polymer can be difficult to control and can occur too quickly for a given patient, increasing the risk of soft tissue pull-out. Further, resorbable materials have been shown to induce fibrous tissue formation between the resorbable implant and the bone, increasing the risk of soft tissue pull-out. This may be due to the local chemistry created as the polymer dissolves.

What is needed in the art is an orthopaedic screw that allows for more effective fixation of the tissue and visualization with known imaging devices of the tissue near and surrounding the screw.

SUMMARY OF THE INVENTION

The present invention provides porous screws and screws that can deliver therapeutic agents. Further, the present invention provides a porous screw for attaching various soft tissues to bone, and/or for attaching bone to bone, and/or for delivering therapeutic agents (for example biologics or drugs) to soft tissue and/or bone. Potential uses include, but are not limited to, ACL and PCL reconstruction, medial collateral ligament repair, lateral collateral ligament repair, posterior oblique ligament repair, iliotibial band tenodesis reconstruction, patellar ligament and tendon repair, pedicle screws for spine repair, bone fracture fixation screw, and drug eluting implant (non-load bearing) for delivery of therapeutics.

One embodiment of the present invention provides an orthopaedic screw having a plurality of regions, at least one of which may be porous. The orthopaedic screw includes a head, a tip and at least one thread. The porosity of the screw of the present invention can vary within the part or region, including changes in pore shape, size and density. These characteristics can vary along the length of the screw axis and/or radially (from the outer diameter to the axis).

The orthopaedic screw of the present invention may further include at least one solid region formed of any implantable polymer, reinforced polymer or metal. The solid region of material may be, for example, at the outer portion of the threads and the leading tip of the screw due to the high stresses present during insertion. The solid region may further include the head of the orthopaedic screw of the present invention.

The materials to create the orthopaedic screw of the present invention can be any implantable polymer, metal or ceramic, or any combination thereof. Possible polymers include polyetheretherketone (PEEK), polyetherketone (PEK), polyaryletherketone (PAEK), polyethylene, and resorbable polymers such as polylactic acid (PLA) and polyglycolic acid (PGA).

The thread of the orthopaedic screw of the present invention may be continuous or discontinuous and be a single or multiple lead thread. The inventive screw may further be cannulated or non-cannulated.

The orthopaedic screw of the present invention may further be used to locally deliver therapeutic agents that promote positive tissue response (e.g. increased growth rate, decreased inflammatory response). Such therapeutic agents include, but are not limited to, hydroxyapatite, drugs and biologics.

A second embodiment of the orthopaedic screw of the present invention provides for immediate delivery of a therapeutic agent through channels and/or holes and reservoirs for long-term delivery of a therapeutic agent. Access to the delivery channels, holes and/or reservoirs may be gained by provision of a self-sealing polymer diaphragm which can allow for direct interface with a needle at the time of surgery of post-surgery. Alternatively, a removable cap made of PEEK or other implantable material may provide access to and seal the medicine delivery features of the inventive screw.

A third embodiment of the inventive orthopaedic screw composed of radiolucent material includes a radiopaque marker to indicate position and orientation of the implant on an x-ray, fluoroscope, or similar diagnostic tool. The markers can be made of any number of more dense implantable materials. Options include, but are not limited to implantable metals (stainless steel, titanium, or titanium alloys for example), barium sulfate filled PEEK, carbon filled PEEK, and other polymers with radiopaque material (such as barium sulfate or zirconium dioxide). Examples of the marker structure include one or more of the following: a pin filling some or all of the cannula of a cannulated screw, one of material layers of the inventive screw if manufactured by layering, all or some of the threads, a cross pin, or the head or tip of the screw. The opacity and/or amount of radiopaque material can be controlled so that the marker does not prevent evaluation of the tissue near the screw by x-ray or other diagnostic methods.

An advantage of the present invention is that the porous nature of the inventive orthopaedic screw and the ability to deliver therapeutic agents to the surrounding tissue promotes successful tissue integration. Such local delivery of therapeutic agents can aid in such issues as improving the attachment strength of soft tissue to bone in reconstructive surgeries, improving the attachment strength of bone to screw, and strengthen bone in osteoarthritic or osteoporotic patients.

Another advantage is that the orthopaedic screw of the present invention can effectively be utilized for long term or short term delivery of therapeutic agents. Another advantage is that the therapeutic agent can be pre-loaded into the device at the factory or loaded by the surgeon before, during or after surgery.

BRIEF DESCRIPTION OF THE DRAWINGS

The above-mentioned and other features and advantages of this invention, and the manner of attaining them, will become more apparent and the invention will be better understood by reference to the following description of embodiments of the invention taken in conjunction with the accompanying drawings, wherein:

FIG. 1 is a section view of a porous screw with solid outer threads and tip according to the present invention;

FIG. 2A shows a view of a screw having a continuous thread;

FIG. 2B shows a view of a screw having a discontinuous thread;

FIG. 3 illustrates an implant according to the present invention for immediate delivery of a therapeutic agent;

FIG. 4 illustrates an implant according to the present invention for immediate or sustained delivery of a therapeutic agent;

FIG. 5 illustrates a therapeutic agent delivery implant according to the present invention with sealing cap;

FIG. 6 illustrates an implant according to the present invention with port attachment features;

FIG. 7A illustrates an implant according to the present invention including a radiopaque marker;

FIG. 7B illustrates an implant according to the present invention including a radiopaque marker; and

FIG. 7C illustrates an implant according to the present invention including a radiopaque marker.

Corresponding reference characters indicate corresponding parts throughout the several views. The exemplifications set out herein illustrate embodiments of the invention and such exemplifications are not to be construed as limiting the scope of the invention in any manner.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a device which can have a porous nature and which has the ability to deliver therapeutic agents. The porous nature of the device of the present invention and the ability of the device of the present invention to deliver therapeutic agents therethrough addresses existing deficiencies in the known art by promoting successful tissue integration.

The present invention provides a screw that is porous and/or can deliver therapeutic agents to the surrounding tissue. The materials to create this screw can be any implantable polymer, metal or ceramic or combinations of these. Possible polymers include PEEK (Poly(etheretherketone)), PEK (Poly(etherketone)), PAEK (poly(aryletherketone)), polyethylene, and resorbable polymers such as PLA (Poly(lactic acid)) and PGA (poly(glycolic acid)). Likely first candidates are PEEK, reinforced PEEK (reinforcing materials include but are not limited to carbon fiber/particles/nanotubes, barium sulfate, zirconia) and titanium/titanium alloys. The screw of the present invention can include, but does not need to include, the ability to deliver therapeutic agents (such as drugs or biologics) to the surrounding tissue. The therapeutic agent can be selected by the surgeon before the surgery, at the time of surgery, or at any point in time thereafter. In addition, the therapeutic agent can be pre-loaded into the device at the factory through currently acceptable practices or loaded by the surgeon before, during, or after surgery (as a follow-up procedure).

The screw of the present invention can be porous but does not need to be porous.

I. Porous Structure—Design Options According to the Present Invention

Screw 10 of the present invention can be fully porous or have select regions of solid material. For example, screw 10 may include porous region 12 and a solid region of material at the outer portion of threads 14 and leading tip 16 of screw 10. The solid region of material at the outer portion of threads 14 and leading tip 16 of screw 10 may be desired due to the high stresses these regions can see during screw insertion (see FIG. 1). In addition, a very rough porous structure on the outer portion of the threads can cause insertion of the screw to be difficult due to its potential to grab versus slide past or cut through bone/soft tissue. In another example, the head (not shown) of screw 10 may be solid. This solid material can be formed of any implantable polymer, reinforced polymer, or metal.

Thread 14 can be continuous (see FIG. 2A) or discontinuous (see FIG. 2B) and be a single or multiple lead thread.

The porosity of the screw can vary within the region(s), including changes in pore shape, size, and density. These characteristics can vary along the length of the screw axis and/or radially (from the outer diameter to the axis).

Delivery of Therapeutic Agents

Another way of improving integration of the surrounding tissue is to deliver therapeutic agents that promote positive tissue response (e.g. increased growth rate, decreased inflammatory response). The orthopaedic screw of the present invention can be used to locally deliver such therapeutic agents to the tissue surrounding the device. Such local delivery of therapeutic agents can aid in such issues as improving the attachment strength of soft tissue to bone in reconstructive surgeries, improving the attachment strength of bone to the screw, and strengthen bone in osteoarthritic or osteoporotic patients. Therapeutic agents include, but are not limited to, hydroxyapatite, drugs, and biologics.

Screws allowing for localized delivery of therapeutic agents, according to the present invention, can be, but need not be, porous. Porous screws according to the present invention can, but need not, allow for localized delivery of therapeutic agents.

Screw 10 can contain reservoirs 18 for the long-term delivery of the therapeutic agents, as illustrated in FIG. 4 and/or channels/holes 20, as illustrated in FIG. 3, for immediate, local delivery of therapeutic agents. Screw 10 can further include a plurality of interconnected pores (22) allowing for local delivery of a therapeutic agent to the surrounding tissue, as shown in FIG. 4. These options are described as follows:

-   -   1. Long term delivery.         -   a. Reservoirs. One or more reservoirs 18 can allow for the             long term (hours to weeks) delivery of the therapeutic             agents. Access to delivery channels 20, reservoir 18, etc.             of screw 10 is gained by several ways including:             -   i. Self-sealing polymer diaphragm 24 can allow for                 direct interface with a needle at the time of surgery or                 post-surgery (see FIG. 4).             -   ii. A removable cap 26 made of PEEK or another                 implantable material can also provide access to the                 therapeutic agent delivery features and seal these                 features after delivery of the therapeutic agent (FIG.                 5). A tool that facilitates insertion of the screw could                 also aide in assembling cap 26 to the screw.         -   b. Connect to another device. Access to the therapeutic             agent delivery features of the screw can be provided by             interfacing screw 10 with a device designed to deliver             therapeutic agents from subcutaneous to elsewhere in the             body (e.g. a port that is frequently used to deliver             therapeutic agents from sub-skin to a vein deeper in the             chest cavity). The last option can include attachment             feature 28 on screw 10 that directly interfaces with port             30, interfaces with catheter 32 (which interfaces with the             port 30) or interfaces with an additional component, which             can be attached to screw 10 to interface with port 30 or             catheter 32—See FIG. 6).     -   2. Immediate delivery. No reservoir is required for this         approach. The access means of the reservoir design above         (self-healing polymer diaphragm 24 and removable cap 26) can         also be used to access delivery channels 20 in this design. This         design can also include a simple interface with a delivery tool.         An example of this is a simple slip fit between a delivery         needle and the screw's cannula.     -   A given screw can contain any or all of these options.

Cannulation

The screws can be cannulated or non-cannulated.

Radiopaque Markers—Polymer Implants

If the implant according to the present invention is made of a radiolucent material (for example polymers such as PEEK), radiopaque markers 34 can be included to indicate position and orientation of the implant on an x-ray, fluoroscope, or similar diagnostic tool. Markers can be made of any number of more dense implantable materials. Options include, but are not limited to, implantable metals (stainless steel, titanium, or titanium alloys for example), barium sulfate filled PEEK, carbon filled PEEK, or other polymers with radiopaque material (such as barium sulfate or zirconium dioxide). Examples of the marker design include one or more of the following: pin 36 filling some or all of cannula 38 of a cannulated screw, one of the material layers if the manufacturing method involves material layering (discussed below), all or some of threads 14, cross pin 40, or head 42 or tip 16 of the screw (see FIGS. 7A-C). The opacity and/or amount of radiopaque material can be controlled so that the marker does not prevent evaluation of the tissue near the screw by x-ray or other diagnostic ways (as occurs with current solid metal screws).

II. Porous Structure—Manufacturing Options According to the Present Invention

The porous structure of the present invention can be manufactured using a variety of methods. These manufacturing options according to the present invention include seven options as follows:

-   -   1. Rolled. A porous sheet can be, for example, rolled into a         screw. This is essentially the reverse of making a radial,         spiral cut that is parallel to the axis of the screw. Layers of         different materials can be combined in this process. This         process involves the following:         -   a. Make a porous sheet with holes in a pattern so that they             line up when rolled.         -   b. Roll sheet. This step can be performed with or without             the aid of a center mandrel or rod.             -   1. The sheet can be rolled without the aid of any center                 mandrels. This can create a cannulated screw. A                 biocompatible pin/rod can be inserted in any center hole                 and bonded to the screw to create a non-cannulated                 screw.             -   2. The sheet can be rolled around a removable mandrel.                 This can create a cannulated screw. A biocompatible                 pin/rod can be inserted in any center hole and bonded to                 the screw to create a non-cannulated screw.             -   3. Alternately the sheet can be rolled around and bonded                 to a biocompatible rod, creating a non-cannulated screw.         -   c. Bond the rolled material.     -   2. Spiraled layers. This method is similar to the rolled         approach, but this method involves bands of material that are         wrapped around one another. The main difference between this         method and that of rolling is that in this method, the bands of         material translate along the axis while they are wrapped. Bands         of several materials can be combined and intertwined. All bands         can have the same direction and pitch of winding or different         directions and pitches. These bands can be wrapped around a         mandrel that is later removed to aid in bonding and to create a         cannula. They can also be wrapped around a pin which they are         then bonded to, creating a non-cannulated screw. An alternate         option for creating a non-cannulated screw is to create the         screw with or without the aid of a mandrel, then insert and bond         a pin within the center hole of the screw.     -   3. Layered/stacked. Make a number of layers that are stacked and         bonded to create the screw. These layers can be parallel to one         another. The faces of the layers are perpendicular to the axis         of the screw, parallel to it, or any other angle of orientation.         To reduce secondary operations, alignment of one layer to         another may be desirable. Alignment of layer to layer can be         achieved by such ways as alignment fixtures that line up the         center cannula (if the screw is cannulated) of each layer to one         another (by way of a pin for example), fixtures or implant         components/features that align pore or thread features to one         another, or fixtures or implant components/features that align         features on the outer diameter of each layer to one another.         Features can also be created within a given layer to aid in         alignment and/or assembly (such as grooves and mating         protrusions).         Note: The holes in options 1-3 can be created by, for example,         laser cutting, punching, etching, electrical discharge         machining, plasma etching, electroforming, electron beam         machining, water jet cutting, stamping, or machining. For         polymer based materials, they can be created as the sheets are         created by, for example, extruding, injection molding, or hot         stamping.     -   4. Dissolvable Material.         -   a. One method involves creating a mixture of powdered             implantable material (e.g. PEEK) and a powder (e.g. salt)             that is soluble in something in which the implantable             material is not soluble (such as water, isopropyl alcohol             for the PEEK example). The mixture is then heated to bond             the implantable particles together. Pressure can also be             applied to aid in the bonding of particle to particle. Heat             can be created by convection or other ways (such as coating             the powder with a material that absorbs a given range of             energy waves—such as laser waves—and causes heating. (e.g.             Clearweld coating by Gentex® Corporation)). Finally,             dissolve away the filler to create the porous implantable             material. This method can create net shape parts or raw             material shapes from which individual parts can be created.         -   b. Another method involves mixing an implantable polymer             with a dissolvable material such as described above. The             mixture is then pelletized and then injection molded to an             intermediary or the final part shape. The filler is             dissolved away to create the porous implantable polymer.     -   5. Stereolithography.     -   6. Laser or Electron Beam Sintering of Powdered Material.     -   7. A combination of the above methods: for example, using the         dissolvable method to create microporous sheets of PEEK, then         stamping larger pores and stacking to create a screw.

III. How to Bond Parts Containing Polymer(s)

Options for Bonding Processes

-   -   1. Heat. Heat can be generated in several ways:         -   a. Ultrasonic welding—use ultrasonic waves to create heat at             the interface of layers.         -   b. Heat staking—use a heated tool to cause melting between             the layers.         -   c. Vibratory welding.         -   d. Laser welding.         -   e. Convection—use an oven to create heat to cause bonding.         -   f. Intermediary layer—for example, use a material that can             absorb energy waves that pass through the polymer (for             example PEEK) without causing damage. The absorbed energy             will cause localized heating. An example of such a coating             is Clearweld by Gentex® Corporation. The laser waves that             Clearweld absorbs pass through the PEEK without causing             damage, allowing the layers to be melted together without             large scale damage to the PEEK.     -   2. Chemical.         -   a. Adhesives—a secondary material (such as adhesive) can be             used to bond the material.         -   b. Solvent bonding—a material in which the polymer or             reinforced polymer is soluble can be applied to the sheet             surfaces allowing multiple surfaces to be bonded to one             another.         -   c. Overmolding—overmolding of the polymer or reinforced             polymer can provide a chemical bonding     -   3. Mechanical.         -   a. Overmolding—overmolding of a polymer or reinforced             polymer can create a mechanical lock between components on a             micro or macro scale (microscale—the molded material locks             with surface asperities of the existing material.             Macroscale—features such as tongue-groove connections or             undercuts). The overmolded material can be a separate             component from the layers or one layer can be overmolded             onto another layer.         -   b. Features are provided within the layers or by a separate             component which provides a mechanical lock—e.g. a pin, snap             lock connection, dove-tail, tongue-groove, rivet, melting             tabs to create a mechanical lock, etc.         -   c. Some adhesives provide a mechanical bond in addition to             or instead of a chemical bond.     -   4. Combinations of Any/All of the Above Methods.

Order of Processes

-   -   1. Bond all layers together at once—especially attractive for         methods utilizing energy waves to trigger bonding (e.g.         Clearweld coating by Gentex® Corporation or ultraviolet light         curable adhesives).     -   2. Simultaneously bond and roll/stack layers at once—again, may         be especially attractive for methods utilizing energy waves to         trigger bonding (e.g. if light cannot penetrate all layers of a         rolled design in order to activate an adhesive, the rolling         operation could take place in a light box allowing for a         continuous rolling and adhesive curing operation.     -   3. Roll/stack layers and bond in increments. This could add a         single layer at a time or multiple layers.

IV. How to Bond Metal/Metal Alloy Parts

Options for Bonding Processes

-   -   1. Heat.         -   a. Laser welding—layers can be laser welded in a number of             locations. Two or more layers or wraps of material can be             welded together at once depending on the size of the part             and alignment of the pores (the laser can access several             layers to be bonded through the porosity).         -   b. Spot welding—traditional spot welding can be used to bond             two or more layers/wraps of material.         -   c. Diffusion bonding/sintering.         -   d. Vibratory welding.         -   e. Ultrasonic welding.     -   2. Adhesives.     -   3. Mechanical ways. Features are provided within the layers or         by a separate component which provides a mechanical lock—e.g. a         pin, snap lock connection, dove-tail, tongue-groove, rivet,         melting tabs to create a mechanical lock etc.     -   4. Overmolding with an implantable polymer. Overmolding of PEEK         or another implantable polymer can create a mechanical lock         between components on a micro or macro scale (microscale—the         molded material locks with surface asperities of the existing         material. Macroscale—features such as tongue-groove connections         or undercuts). The overmolded material can be a separate         component from the layers or one layer can be overmolded onto         another layer.

Order of Processes

As with the polymer materials discussed above, two or more layers of metal can be bonded during increments or as a continuous stacking/bonding process.

V. Making Threads—Manufacturing Options According to the Present Invention

-   -   1. Form the threads after the layers have been bonded to create         a screw blank (see FIG. 13)         -   a. Machine the threads         -   b. Hot form the threads with a mold     -   2. Form threads in the sheets prior to bonding.         -   a. Rolling method: The material will not actually create the             complete thread shape until the sheets are formed into the             final shape. Continuous or discontinuous threads can be             created. Design options for this method include creating             raised material that forms the threads or removing material             to leave the thread material. The raised material in the             first method can be created by way of machining, laser             ablation, hot stamping, hot or cold forming, chemical             etching, electro-discharge machining and similar methods.             The material of the second method can be removed by way of             machining, laser cutting, stamping, etching, punching,             electro-discharge machining, water jet cutting, electron             beam machining or other means.         -   b. Stacking method: Continuous or discontinuous threads can             also be created by this method. The ‘ears’ of material in             each layer form the threads when the layers are stacked.             These can be created by way of machining, hot stamping, hot             or cold forming, dies/punches, chemical etching,             electro-discharge machining and similar methods.     -   3. Add separate threads—Threads can be formed separately and         attached to the screw blank. The material for these threads can         include: biocompatible polymers, reinforced biocompatible         polymers and/or biocompatible metals. The attachment ways for         these threads include:         -   a. Mechanical attachment—press/interference fit, tabs.         -   b. Overmolding—mold the solid, porous, or reinforced polymer             screw inside of the solid threads or mold the porous, solid             or reinforced polymer threads onto the already formed screw.         -   c. Adhesive or solvent bonding.

VI. Cannulation—Manufacturing Options According to the Present Invention

With any of the manufacturing methods, screws can be created with or without a cannula.

-   -   1. Cannulated.         -   a. Rolling method. In this method, it can be desirable to             wind the material around a mandrel that is at the center of             the screw, running along its axis. This mandrel can be             removed to leave an open cannula.         -   b. Layered method. A center hole at the axis of each layer             is created to form the cannula when they are stacked             together.     -   2. Non-cannulated.         -   a. Rolled method.             -   i. The sheet can also be bonded to the mandrel, with the                 mandrel forming a portion of the implant. This mandrel                 can be solid or porous and of any implantable material                 such as PEEK or titanium.             -   ii. In addition, the material can be formed around a                 removable mandrel, creating a cannula. This cannula can                 be then be filled with a biocompatible material that is                 attached/bonded to the screw.         -   b. Layered method. The layers that are stacked to create the             screw can have solid material in place of the holes that             would create the cannula. Alternately, they can have             cut-outs creating the cannula and this cannula can be filled             with a biocompatible material that is attached/bonded to the             screw.

While this invention has been described with respect to at least one embodiment, the present invention can be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practice in the art to which this invention pertains and which fall within the limits of the appended claims. 

What is claimed is:
 1. An orthopaedic device comprising: a therapeutic agent; and a screw having a reservoir and a plurality of porous bands in fluid connection with said reservoir and extending from said reservoir to an outside surface of the screw, said plurality of porous bands being separated by at least one non-porous region of the screw, said screw configured to deliver said therapeutic agent from said reservoir through said plurality of porous bands to a surrounding tissue when said screw is implanted in said tissue.
 2. The orthopaedic device of claim 1, wherein said therapeutic agent is one of hydroxyapetite, drugs and biologics.
 3. The orthopaedic device of claim 1, further comprising a self-sealing diaphragm configured for injection of said therapeutic agent into said screw.
 4. The orthopaedic device of claim 1, further comprising a removable self-sealing cap configured for sealing said screw after delivery of said therapeutic agent.
 5. The orthopaedic device of claim 1, further comprising a port and a catheter, wherein said screw is configured to receive said therapeutic agent through said port.
 6. The orthopaedic device of claim 1, wherein said screw is cannulated.
 7. The orthopaedic device of claim 1, wherein said plurality of porous band include at least one first set of said plurality of interconnected pores and at least one second set of said plurality of interconnected pores, said at least one first set of said plurality of interconnected pores and said at least one second set of said plurality of interconnected pores being configured to deliver said therapeutic agent from said screw to said surrounding tissue.
 8. The orthopaedic device according to claim 1, wherein said screw is non-cannulated. 